| Architectural
Mutli-Purpose Epoxy Based Primer |
Formulated under ISO9001 &
ISO14000 Architectual
Coating Manufacturing System
ISO 9000 : 2000 Standard Certification No. 00704Q11192ROS
ISO 14000 : 1996 Standard Certification No. 00705E10022ROS |
| |
|
| Description: |
|
| |
A two pack amide cure architectural epoxy pigmented
primer especially developed to provide optimum
base for high-performance architectural top-coats
of Polyurethane finishes. It is marked by extreme
adhesion and high resistance to moisture and chemicals.
This primer supplied in a range of standard colours
to advance the opacity of the topcoat, Also, sanding
propertiesare excellent, with minimum treatment,
very smooth surfaces and touch dry within 25 mins
at normal temperature.
It may be sanded and topcoated after 4 - 5 hours
drying depend on temperature
and humidity. |
| |
|
| Use: |
|
| |
Suitable for using on varies kind of substrate,
metal, concret, ceramic, wood, cement render,
particle board and fibreglass, etc
Also, it is recommended as surfacer for zinc
rich primer intended for total high
performance system.
|
| |
|
| Base: |
|
| |
Epoxy and Polyamide Resin
I.A.T.A. - D.G. Regulations - UN 1993
International Air Transport Association D.G. Certificate
000129QCO HK |
| |
|
| Colour: |
|
| |
Selected colour range
For other special request, please contact our Technical
Dept. |
| |
|
| Finish: |
|
| |
Matt |
| |
|
| Flash Point: |
|
| |
Below 90F (32 C) |
| |
|
| Volume Solid: |
|
| |
Approx 55% |
| |
|
| Mixing Ratio: |
|
| |
The base and catalyst components are supplied
in separate containers at correct mixing ratio of
Part A base component 4.0 by vol
Part B Catalyst component 1.0 by vol |
| |
|
| |
|
| Architectural
Mutli-Purpose Polyurethane Coating |
Formulated under ISO 9001 &
ISO 14000 Architectural
Coating Manufacturing System.
|
| |
|
| Description: |
|
| |
A two pack polyurethane and
isocyanate fast curing P.U. coating especially
designed for ceramic, metal (outdoor architectural
matel panels - V.E. panel) and concrete area.
This polyurethane coating provide excellent film
performance,
weathering resistant for outdoor exposure, wet
scrub resistant
for rountine cleaning and good general properties
for protection
and decoration.
This 2 K P.U. has very fast touch free drying
time, easy application
and good adhesion on all primed surfaces. |
| |
|
| Use: |
|
| |
Suitable for using on varies kind of primed substrate
of metal, ceramic, concrete, wood and some selective
plast materials. (Please contact our technical dept.
for more details)
This coating can be both cold cure and forced drying
in oven with
80C - 45 mins. |
| |
|
| Base: |
|
| |
Polyol and Isocyanate Hardener
I.A.T.A. - D.G. Regulation - UN 1993
International Air Transport Association
D.G. Certification 000129QCO HK |
| |
|
| Colour: |
|
| |
Assorted Colour range
For other special request, please contact our Technical
Dept. |
| |
|
| Finish: |
|
| |
Full-gloss / Semi-gloss |
| |
|
| Flash Point: |
|
| |
Below 72F (22C) |
| |
|
| Volume Solid: |
|
| |
Approx 50-55% varies on colour |
| |
|
| Mixing Ratio: |
|
| |
The base and catalyst components arre supplied
in separate
containers at correct mixing ratio of
Part A Base Component 2 parts by vol
Part B Catayst Compnent 1 part by vol
Add the catalyst to the base component with mechanical
mixing, After mixing a 8 - 10 minutes should elapse
before apply on the substrate |
| |
|